Self-piercing rivet and self-piercing riveting method and self-piercing riveted joint

ABSTRACT

A self-piercing rivet for connecting high-strength steels. The rivet having a head which has a head diameter (DH); a shank which has a shank diameter (DS); and, located at the foot end of the shank opposite the head, the shank has radially outward a flat surface section and radially inward an axial recess defining an axial depth (LB). The ratio of axial depth (LB) of the recess to the shank diameter (DS) is smaller than 0.3.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of international applicationPCT/EP2014/072452, filed Oct. 20, 2014 which claims priority from GermanPatent Application No. DE102013020504.2 filed Dec. 11, 2013, thedisclosures of which are incorporated herein by reference in theirentirety.

BACKGROUND OF THE INVENTION

The present invention relates to a self-piercing rivet for connectinghigh-strength steels, with a head which has a head diameter and with ashank which has a shank diameter, wherein, at the foot end opposite thehead, the shank has an axial recess which has an axial depth, andwherein, at the foot end the shank has a flat surface section.

Furthermore, the present invention relates to a self-piercing rivetedjoint with at least one upper workpiece and one lower workpiece, ofwhich at least one is formed from a high-strength steel, and with adeformed self-piercing rivet of the type referred to above, the head ofwhich bears against the upper workpiece.

Finally, the present invention relates to a method for producing such aself-piercing riveted joint, with the steps of providing a workpiecearrangement which has at least one upper and one lower workpiece, and ofdriving a self-piercing rivet of the type referred to above into theworkpiece arrangement with a punching force.

A self-piercing rivet of the form referred to above is known from EP 1229 254 A2. In this document, it is proposed to provide a self-piercingriveted joint with at least two joining parts made of a high-strengthsteel, which are connected to each other by means of a semi-tubularself-piercing rivet which is formed from steel and which has a rivethead and an adjoining rivet shank with a rivet foot on the end side,wherein the rivet foot is of truncated design in the initial statebefore the joining operation. The shape of the self-piercing rivet is inthis case intended to be identical to the shape of a self-piercing rivetas is known also for joining light metal workpieces, specifically fromEP 0 833 063 A1. The truncated design of the rivet foot is intended toachieve a favourable deformation behaviour of the semi-tubularself-piercing rivet during the joining of the high-strength joiningparts, wherein the endeavour of the rivet shank to expand is reduced incomparison to a pointed rivet foot. The expansion here is intended totake place only when the rivet shank pierces with the rivet foot intothe lower joining part. The joining parts are intended to have a tensilestrength of greater than 500 N/mm² to up to 1500 N/mm². The tensilestrength of the semi-tubular self-piercing rivet used is intended to liewithin a range of between 1200 and 1400 N/mm², but can even reach valuesof up to 2000 N/mm².

In order to ensure a suitable expansion behaviour, the quotient from theaxial depth of the shank cavity and the outside diameter of the rivetfoot is to lie between 0.3 and 0.7. At too small an axial depth of theshank cavity, the rivet shank will not expand sufficiently afterperforating the upper steel sheet.

A further semi-tubular self-piercing rivet is known from WO 2007/132194A1. The shank here is to be provided with a central blind hole bore,wherein the ratio of a difference between an outside diameter and aninside diameter of the shank in the region of the bore to the outsidediameter of the shank is intended to lie within the range of 0.47 to0.52.

Furthermore, EP 2 314 890 A2 discloses a semi-tubular self-piercingrivet for connecting high-strength and super-high-strength steels,wherein a head diameter is generally smaller than or equal to 1.3 timesthe shank diameter.

However, as before, prior-art self-piercing riveted joints, with whichhigh-strength or super-high-strength steels are connected, may havediverse problems. Firstly, the extent of the expansion may not besymmetrical with respect to a rivet axis. Furthermore, the shank may becompressed and twisted. In some cases, it is not even possible to pressthe rivet into the workpiece arrangement, with it even being possiblefor the self-piercing rivet to be fractured.

BRIEF SUMMARY OF THE INVENTION

Against this background, it is an object of the invention to specify animproved self-piercing rivet, an improved self-piercing riveted jointand an improved self-piercing riveting method, which are suitable forconnecting high-strength and super-high-strength steels.

This object is achieved in the case of the self-piercing rivet referredto at the beginning in that the ratio of axial depth of the recess toshank diameter is smaller than 0.3, in particular smaller than 0.28, andparticularly preferably smaller than 0.25, or even smaller than 0.2.

The ratio of axial depth of the recess to shank diameter is preferablygreater than 0.05, and preferably greater than 0.1, and in particulargreater than 0.12.

Furthermore, the above object is achieved by a self-piercing rivetedjoint with an upper workpiece and with a lower workpiece, of which atleast one is formed from a high-strength steel, and with a deformedself-piercing rivet, the head of which bears against the upperworkpiece, wherein the self-piercing rivet is in particular aself-piercing rivet according to the invention.

Finally, the above object is achieved by a method for producing aself-piercing riveted joint, in particular a self-piercing riveted jointof the type referred to above, with the steps of providing a workpiecearrangement which has at least one upper and one lower workpiece, and ofdriving a self-piercing rivet of the type according to the inventioninto the workpiece arrangement with a punching force.

By means of the configuration according to the invention of theself-piercing rivet, a deformation of the self-piercing rivet that isless focused on an expansion of the rivet shank is produced during theself-piercing riveting method. Rather, the effect achieved by therelatively short axial depth of the recess is that the connection isformed by an upsetting operation of the rivet, said upsetting operationbeing caused in particular by the counter pressure of the high-strengthsteel of the workpiece arrangement. The undercut which is thereby formedcan be relatively small in this case. However, owing to thehigh-strength materials, even a relatively small undercut is sufficientin order to realize the required connection strength.

In addition, the effect achieved by the relatively small axial depth ofthe recess is that the self-piercing rivet obtains a significantlygreater stability which makes it possible to pierce through evenhigh-strength and super-high-strength steels.

A contribution to the new manner of producing self-piercing rivetedjoints is provided by the flat surface section at the foot end. In otherwords, it is preferred if the generally annular end side of the footend, which end side is also referred to as a cutting edge, is of atleast proportionally flat design, specifically is preferably orientedperpendicularly to a longitudinal axis of the self-piercing rivet.

The upper workpiece of the workpiece arrangement is preferably producedfrom steel and has a tensile strength which is preferably greater than800 N/mm², in particular greater than 1000 N/mm². The tensile strengthsat least of the upper workpiece can be up to 1500 N/mm² and beyond.

The tensile strength of the lower workpiece—without heating—ispreferably limited to approximately 600 N/mm².

In other words, even forming steels, such as are known under the name“Usibor®”, in which, before a heat treatment, the microstructureconsists in particular of a ferritic—pearlitic structure, can be joinedwith the required connection strength by the self-piercing rivetaccording to the invention.

It goes without saying that the strength or hardness of theself-piercing rivet is correspondingly adapted. Furthermore, it goeswithout saying that the self-piercing rivet is a semi-tubularself-piercing rivet which is produced in particular rotationallysymmetrically and/or as a single piece from steel.

A small radius of 0.5 mm or less is preferably provided at thetransition from the shank to the head in order to keep the settingforces as small as possible.

The minimum rivet length is preferably the thickness of the upperworkpiece plus a length which is preferably greater than 2 mm and inparticular equal to 3 mm. The maximum rivet length preferably lieswithin the range of the thickness of the workpiece arrangement.

The object is therefore completely achieved.

It is particularly preferred if the recess is frustoconical inlongitudinal section.

In this alternative, the diameter of the recess in the region of thefoot end is preferably greater than the diameter in the region of a baseof the recess. In this embodiment, the base of the recess is preferablyflat, but can also be curved concavely or convexly.

According to a further preferred embodiment, the recess is arch-shapedin longitudinal section.

The arch shape here can be produced by a single radius, and thereforethe recess is in the shape of an arc of a circle in longitudinalsection.

However, it is particularly preferred if the recess is in the shape of apointed arch or a gothic arch in longitudinal section.

Such an arch shape is produced by two arcs constructed from circles andhaving a point.

It is preferred here if the point is rounded by means of a radius in asuitable manner.

Furthermore, it is preferred in the case of the pointed arch shape ifthe center points of the respective arcs, as the respectively assignedarch, each lie on different sides—as seen in longitudinal section—of alongitudinal center axis of the self-piercing rivet.

In the two embodiments referred to above—frustoconical or arch-shaped,it is advantageous for the punching forces acting from the head end tobe suitably introduced into the foot end.

Overall, it is furthermore preferred if the recess does not have acylindrical section.

A cylindrical section in the recess can result in instability andpossibly in fracturing at very high punching pressures.

The stability of the self-piercing rivet can be increased overall byomitting a cylindrical section within the recess.

According to a further embodiment which, in conjunction with theprecharacterizing clause of claim 1, constitutes a separate invention,the recess has a recess volume, wherein a ratio of recess volume tovolume of the shank is smaller than 0.25, in particular smaller than0.18 and/or is greater than 0.05, in particular greater than 0.1.

The recess volume in this case is calculated starting from the foot endof the self-piercing rivet. The volume of the shank is that volume ofthe shank at which the shank has a uniform outside diameter, i.e.exclusively a possible transition section to a head of the self-piercingrivet, but including the recess volume which is consequently containedin the volume of the shank.

The relatively small recess volume results, firstly, in great stabilityof the self-piercing rivet. Secondly, a punched-out piece detached fromthe upper workpiece is not received by the recess, but rather is pressedin front of the rivet by the rivet during the punching operation. Theeffect which can advantageously be achieved by this means is thatgreater deformation of material takes place within a die of aself-piercing riveting tool instead of deformation in the recess.

According to a further preferred embodiment, the flat surface section isdesigned as an annular surface section and has a radial width in crosssection, wherein the ratio of radial width of the annular surfacesection to shank diameter is greater than 0.05 and/or is smaller than0.25.

The self-piercing rivet is preferably produced from a steel with ahardness of at least 500 HV10 (1630 MPa), in particular with a hardnessof at least 650 HV10, in particular with at least 700 HV10. The hardnessis generally smaller than 800 HV10.

In the self-piercing riveted joint according to the invention, it ispreferred if the axial thickness of the upper workpiece is greater thanor equal to the axial depth of the recess in the undeformed state.

Furthermore, it is advantageous in the case of the self-piercing rivetedconnection according to the invention if a punched-out piece is detachedfrom the upper workpiece, and if less than 50% of the volume of thepunched-out piece is located within the deformed recess, in particularless than 30%, preferably less than 25% and particularly preferably lessthan 20%.

This results in the self-piercing rivet being designed in such a mannerthat it is substantially upset, as a result of which the volume of therecess is reduced, and therefore the punched-out piece is substantiallypushed in front of the rivet during the self-piercing rivetingoperation.

Material of the lower workpiece can thereby be suitably displaced withinthe die by means of the punched-out piece, and therefore said materialflows behind an undercut in the shank of the self-piercing rivet.

All in all, it is furthermore advantageous if the shank of the deformedself-piercing rivet forms an undercut in relation to forces in thedirection of the head, wherein the ratio of undercut to shank diameteris smaller than 0.1 and/or is greater than 0.01.

This results in the extent of the undercut being comparatively small.However, such a small undercut is sufficient when connectinghigh-strength steels in order to realize the necessary connectionstrength.

According to a further preferred embodiment of the self-piercing rivetedjoint, the ratio of axial length of the self-piercing rivet afterdeformation and of axial length of the self-piercing rivet beforedeformation is greater than 0.8 and/or is smaller than 0.95.

This results in the self-piercing rivet only being upset to acomparatively small extent because of the predetermined hardnessthereof, which likewise leads to a relatively small undercut in theradial direction.

This also results in the minimum length of the self-piercing rivetpreferably being produced from the thickness of the upper workpiece plusa value of preferably 3 or 3.5 mm, whereas the maximum length of theself-piercing rivet is preferably calculated by the overall thickness ofthe workpiece arrangement plus 1 mm or is equal to the overall thicknessof the workpiece arrangement.

In the case of the method according to the invention it is advantageousif the workpiece arrangement is supported on a die with a die volumeinto which at least the lower workpiece is driven, wherein the ratio ofdie volume to a volume of the self-piercing rivet is greater than orequal to 1.0 and/or is smaller than or equal to 1.5.

The die volume is the volume into which material at least of the lowerworkpiece flows during the self-piercing riveting operation, wherein theupper edge of the die recess provided for this purpose is substantiallyflush with a supporting surface. The shape of the die recess here ispreferably frustoconical, with a relatively large diameter in the regionof the supporting surface and a smaller diameter in the region of a baseof the die volume.

Overall, the following can furthermore be noted in addition. In the caseof conventional self-piercing riveting, the formation of the undercut isa feature which is relevant to the quality of the connection strength.Owing to the high strength of the rivet according to the invention, thisfeature no longer holds true by itself. The rivet requires a relativelystrong upper workpiece, the punched-out piece of which then upsets therivet and presses it somewhat apart in the process. In contrast torivets from the prior art, the undercut in the connection is notproduced by conventional expansion, but rather is produced by anupsetting operation of the rivet, the upsetting operation being causedby the counter pressure of the high-strength steel. A furtherdifferentiation criterion with respect to conventional rivets is therange of use which, as a rule, begins only at a tensile strength of theupper workpiece of 800 N/mm², in particular of 1000 N/mm². Steels ofthis strength category have found use in vehicle manufacturing becauseof the increased use of lightweight structures made fromsuper-high-strength sheets. The range of use of the self-piercing rivetaccording to the invention downwards is preferably limited by a minimumpunching force—the force for perforating/piercing the high-strengthworkpiece arrangement—of 8 kN. Above said force, a sufficient upsetting(not primarily spreading) of the self-piercing rivet begins, and therequired degree of upset, which is preferably at least 0.15 mm, isachieved. In order to assess the connection quality, the degree of upsetshould also be taken into consideration in addition to the formation ofan undercut. The degree of upset is calculated from the axial length ofthe self-piercing rivet before deformation minus the axial length of theself-piercing rivet after deformation, i.e. in the settled state.

It goes without saying that the features referred to above and thosewhich have yet to be explained below are usable not only in therespectively stated combination, but also in different combinations oron their own without departing from the scope of the present invention.

BRIEF DESCRIPTION OF THE DRAWINGS

Exemplary embodiments of the invention are illustrated in the drawingand are explained in more detail in the description below. In thedrawing:

FIG. 1 shows a longitudinal sectional view through an embodiment of aself-piercing rivet according to the invention;

FIG. 2 shows a longitudinal sectional view through a further embodimentof a self-piercing rivet according to the invention; and

FIG. 3 shows a longitudinal sectional view through a self-piercingriveted joint produced by means of the self-piercing rivet of FIG. 1.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

A rotationally symmetrical semi-tubular self-piercing rivet isillustrated schematically in longitudinal section and denoted in generalby 10 in FIG. 1.

The self-piercing rivet 10 is produced from a strong steel andpreferably has a hardness of greater than 500 HV. The self-piercingrivet is in particular produced by pressure deformation.

The self-piercing rivet 10 has a head 12 and a shank 14 adjoining thelatter in the axial direction. The shank 14 merges into the head 12 viaa transition section 16. An end of the shank 14 that is opposite thehead 12 is designed as a foot end 18 in FIG. 1.

A flat surface section 20 is formed at the foot end 18, said surfacesection being designed as an annular surface section, the outsidediameter of which is limited by an outside diameter of the shank 14 andthe inside diameter of which is limited by an edge of a recess 22 whichextends from the foot end 18 in the direction of the head 12.

In FIG. 1, the recess 22 is of frustoconical design and, starting fromthe foot end 18, has a conically extending recess transition section 24and a recess base 26. The recess base 26 can be of flat design, asillustrated, but may also be of concave or convex design.

Furthermore, the following dimensions are shown in FIG. 1, wherein thepreferred values for said dimension are in each case also plotted in thetable below:

Designation Abbreviation Preferred value Note Axial length,self-piercing LR  5 mm rivet Length, shank LS 3.6 mm Axial height, headLH 0.5 mm Axial depth, recess LB  1 mm Diameter, head DH 7.75 mm Outside diameter, shank DS 5.5 mm Recess diameter at the foot DB 4.5 mmend Recess diameter at the base DB′ ~2.5 mm  Radial width, annular BF0.5 mm surface Section Cone angle, recess αB ~40° i.e. 25°-50° Coneangle, transition αH ~27° i.e. 20°-50° sectionIn the case of the self-piercing rivet of FIG. 1, the ratio of axialdepth LB of the recess 22 to the shank diameter DS is approximately0.18.

The ratio of radial width BF to the shank diameter DS is approximately0.09.

Furthermore, the ratio of the recess volume to the volume of the shankis approximately 0.135, wherein the volume of the recess isapproximately calculated at

VB=(LB·π)/3·[(DB/2)² +DB·DB′+(DB′/2)²],

and wherein the volume of the shank is calculated at

VS=π·(DS/2)²·LS.

The volume VS of the shank consequently includes the recess volume VB.

The values, which are indicated in the table above, for the respectivedimensions and angles can preferably each deviate within the scope ofthe invention upwards and downwards by at least 20%, preferably upwardsand downwards by 10% in each case.

A radius RB which is formed at the transition between the recesstransition section 24 and the recess base 26 is furthermore shown inFIG. 1. The value of RB can be, for example, 0.35 mm. The value of DB′is an approximate value which lies approximately in the center of therecess RB, as seen in the radial direction.

Furthermore, a radius RH which forms the transition between the conicaltransition section 16 and the shank 14 is shown in FIG. 1. The value ofRH can be, for example, 0.5 mm or less.

An alternative embodiment of a self-piercing rivet according to theinvention is illustrated in FIG. 2 and is likewise generally denoted by10. The self-piercing rivet 10 of FIG. 2 corresponds generally inrespect of construction and function to the self-piercing rivet 10 ofFIG. 1. Identical elements are therefore indicated by the same referencenumbers. Essentially the differences are explained below.

The recess 22 of the self-piercing rivet 10 of FIG. 2 is notfrustoconical, as in the case of the self-piercing rivet 10 of FIG. 1,but rather is of arch-shaped design. In more precise terms, the recess22 in FIG. 2 is in the shape of a pointed arch in longitudinal section,the pointed arch being assembled from two arcs of a circle which form apoint on the longitudinal axis. The origins of the arcs of the circlelie in each case on that side of the longitudinal axis which is oppositethe arc of the circle thereof. In the region of the point which isformed by the two arcs of the circle, the recess is rounded with aradius which can be, for example, 0.5 mm. This radius is indicatedschematically in FIG. 2 by R1.

The radius of the two arcs of the circle is indicated schematically inFIG. 2 by R2 and can be, for example, approximately 4 mm.

In the case of the self-piercing rivet 10 of FIG. 2, the maximum axialdepth LB of the recess 22 is preferably approximately 1.5 mm, andtherefore a ratio LB/DS of approximately 0.273 is produced.

The shank diameter DS and the shank axial length LS and also otherdimensions can be identical to those of the self-piercing rivet 10 ofFIG. 1.

A self-piercing riveted joint 30 produced by means of the self-piercingrivet 10 of FIG. 1 is illustrated schematically in longitudinal sectionand is denoted in general by 30 in FIG. 3.

The self-piercing rivet joint 30 connects a workpiece arrangement 32which contains at least one upper workpiece 34 and one lower workpiece36, of which at least the upper workpiece can be produced in the form ofsteel sheet from high-strength or super-high-strength steels.

It is illustrated in FIG. 3 that the self-piercing rivet 10* has cut apunched-out piece 38 out of the upper workpiece 34 and has pressed saidpunched-out piece in front of itself during the self-piercing rivetingoperation. The remaining base thickness between the lower side of thepunched-out piece and the lower side of the lower workpiece 36 isdenoted by 40. This may be, for example, greater than 0.5 mm.

Furthermore, a radial undercut of the deformed shank 14* is shown inFIG. 3. The self-piercing rivet 10* has been upset, in particular in theregion of the foot end, because of the relatively hard material of theupper workpiece 34, and therefore the material of said self-piercingrivet has flowed somewhat outwards radially in the region of the footend. Owing to the great hardness of the self-piercing rivet 10* too, theundercut 42 is nevertheless very small and may be, for example, smallerthan 0.5 mm, but is, as a rule, greater than 0.05 mm. Correspondingly,the ratio of undercut 42 to shank diameter DS is preferably within arange of 0.1 to 0.01.

Finally, FIG. 3 shows a projecting length 44 by which the head 12*protrudes in relation to the upper side of the upper workpiece 34. Theprojecting length 44 is preferably smaller than the axial height LH ofthe self-piercing rivet 10 in the undeformed state.

Furthermore, FIG. 3 shows the axial length LR* of the deformedself-piercing rivet 10*. In the example illustrated, said length can be,for example, approximately 4.4 mm. The ratio of axial length LR* of theself-piercing rivet 10* after deformation and axial length LR of theself-piercing rivet 10 before deformation is preferably greater than 0.8and/or smaller than 0.95.

As stated, the self-piercing rivet 10* has been upset in the region ofthe foot end, and therefore the remaining volume of the remaining recess22* is relatively small. Accordingly, in the embodiment illustrated, atmost a portion of 50%, in particular at most a portion of 25%, of thevolume of the punched-out piece 38 is accommodated within the deformedrecess 22*.

The axial thickness of the upper workpiece 34 is denoted by L34. Saidthickness can be greater than or equal to the axial depth LB of theself-piercing rivet 10 in the undeformed state. The axial thickness ofthe lower workpiece 36 is denoted by L36. Said thickness is preferablygreater than L34. The lower workpiece 36 is preferably softer than theupper workpiece 34.

FIG. 3 furthermore schematically illustrates a die 50 of a self-piercingriveting tool, by means of which an axial force (punching force) 52 isexerted on the upper side of the head 12 of the self-piercing rivet 10during the self-piercing riveting operation. The recess of the die 50 isof approximately frustoconical design. The somewhat softer material ofthe second workpiece 34 is pressed away radially by the punched-outpiece 38 and the die 50 and in this case flows behind the undercut 42such that the self-piercing riveted joint 30 provides an interlockingconnection between the workpieces 34, 36.

The volume of the die recess is preferably greater than or equal to thevolume of the self-piercing rivet 10 in the undeformed state. Inparticular, the ratio of the die volume to the volume of theself-piercing rivet 10 is preferably greater than or equal to 1.0 and/orsmaller than or equal to 1.5.

The minimum punching force 52 is preferably 8 kN.

The minimum length of the self-piercing rivet 10 in the undeformed stateis produced form the thickness L34 plus a value which can be, forexample, 3 or 3.5 mm. The maximum length of the self-piercing rivet 10in the undeformed state can be equal to the overall thickness L34+L36,or a value which is formed to be equal to the overall sheet thickness+avalue of, for example, 1 mm.

The upper workpiece 34 preferably has a tensile strength in the regionof greater than 800 N/mm², in particular greater than 1000 N/mm². Thelower workpiece 36 preferably has a tensile strength of smaller than 600N/mm². The self-piercing rivet 10 preferably has a (Vickers) hardness ofmore than 650 HV.

Although exemplary embodiments of the present invention have been shownand described, it will be appreciated by those skilled in the art thatchanges may be made to these embodiments without departing from theprinciples and spirit of the invention, the scope of which is defined inthe appended claims and their equivalents.

What is claimed is:
 1. Self-piercing rivet (10) for connectinghigh-strength steels, with a head (12) which has a head diameter (DH),and with a shank (14) which has a shank diameter (DS), wherein, at thefoot end (18) opposite the head (12), the shank (14) has an axial recess(22) which has an axial depth (LB), and wherein, at the foot end (18),the shank (14) has a flat surface section (20), characterized in thatthe ratio of axial depth (LB) of the recess (22) to shank diameter (DS)is smaller than 0.3.
 2. Self-piercing rivet according to claim 1,characterized in that the recess (22) is frustoconical in longitudinalsection.
 3. Self-piercing rivet according to claim 1, characterized inthat the recess (22) is arch-shaped in longitudinal section. 4.Self-piercing rivet according to claim 3, characterized in that therecess (22) is in the shape of a pointed arch in longitudinal section.5. Self-piercing rivet according to claim 1, characterized in that therecess (22) does not have a cylindrical section.
 6. Self-piercing rivetaccording to claim 1, characterized in that the recess (22) has a recessvolume, wherein a ratio of recess volume to volume of the shank (14) issmaller than 0.25, in particular smaller than 0.18 and/or is greaterthan 0.05, in particular greater than 0.1.
 7. Self-piercing rivetaccording to claim 1, characterized in that the flat surface section(20) is designed as an annular surface section (20) and has a radialwidth (BF) in cross section, wherein the ratio of radial width (BF) ofthe annular surface section (20) to shank diameter (DS) is greater than0.05 and/or is smaller than 0.25.
 8. Self-piercing rivet according toclaim 1, characterized in that the self-piercing rivet (10) is producedfrom a steel with a hardness of at least 500 HV10.
 9. Self-piercingriveted joint (30) with an upper workpiece (34) and a lower workpiece(36), of which at least one is formed from a high-strength steel, andwith a deformed self-piercing rivet (10*), in particular according toone of claims 1-8, the head (12*) of which bears against the upperworkpiece (34).
 10. Self-piercing riveted joint according to claim 9,wherein the axial thickness (L34) of the upper workpiece (34) is greaterthan or equal to the axial depth (LB) of the recess (22) in theundeformed state.
 11. Self-piercing riveted joint according to claim 9,wherein a punched-out piece (38) is detached from the upper workpiece(34), and wherein less than 50% of the volume of the punched-out piece(38) is located within the recess (22*) of the deformed self-piercingrivet (10*), in particular less than 25%.
 12. Self-piercing rivetedjoint according to claim 9, wherein the shank (14*) of the deformedself-piercing rivet (10*) forms an undercut (42) in relation to forcesin the direction of the head (12*), wherein the ratio of undercut (42)to shank diameter (DS) is smaller than 0.1 and/or is greater than 0.01.13. Self-piercing riveted joint according to claim 9, wherein the ratioof axial length (LR*) of the self-piercing rivet (10*) after deformationand of axial length (LR) of the self-piercing rivet (10) beforedeformation is greater than 0.8 and/or is smaller than 0.95.
 14. Methodfor producing a self-piercing riveted joint (30), in particular aself-piercing riveted joint (30) according to claim 9, with thefollowing steps of providing a workpiece arrangement (32) which has atleast one upper and one lower workpiece (34, 36) and of driving aself-piercing rivet (10) according to one of claim 1 into the workpiecearrangement (32) with a punching force (52).
 15. Method according toclaim 14, wherein the workpiece arrangement (32) is supported on a die(50) with a die volume into which at least the lower workpiece (36) isdriven, wherein the ratio of die volume to a volume of the self-piercingrivet (10) is greater than or equal to 1.0 and/or is smaller than orequal to 1.5.
 16. A self-piercing rivet for connecting high-strengthsteels, the self piercing rivet comprising: a head defining a headdiameter (DH); a shank defining a shank diameter (DS) and including afoot end opposite the head, and radially outward at the foot end theshank further includes a flat surface section facing axially away fromthe head; an axial recess located radially inward of the flat surfacesection, partly defined in the foot end of the shank, open axially awayfrom the head, and frustoconical in longitudinal cross section; theaxial recess defining an axial depth (LB); and the ratio of axial depth(LB) of the recess to shank diameter (DS) is less than 0.3.
 17. Aself-piercing rivet according to claim 16, wherein the axial recessdefines a recess volume (VB), and a ratio of recess volume to a volumeof the shank (VS) is between 0.25 and 0.05.
 18. A self-piercing rivetaccording to claim 16, wherein the flat surface section is an annularsurface section and defines a radial width (BF) in cross section, and aratio of radial width (BF) of the annular surface section to the shankdiameter (DS) is between 0.25 and 0.05.
 19. A self-piercing rivetaccording claim 16, wherein the self-piercing rivet is produced from asteel with a hardness of at least 500 HV10.